I roto i tenei pepa, te painga o te huānga Cu ki te parenga tunu o 8011 ko te konumohe konumohe konumohe i akohia e te whakamatautau tensile, te tirotiro poka, whakamātautau metallographic, me te aukati tunu. The results show that after the baking experiment at 275 ℃ /75s, within a certain range, the high temperature stability of 8011 alloy is improved with the increase of trace Cu content in 8011 koranu.
Tags: 8011 koranu; Cu element; bake resistance
1 trial
1.1 Test material
Ko te 8011 alloy casting and rolling billets were selected as the test materials, and the billet was 7.4mm*1140. The Cu content of the three 8011 Kakano (8011-1, 8011-2, 8011-3) was different, and the composition of other elements was not very different.

1.2 Test plan
The aluminum foil production process flow is: smelting – casting and rolling – hurihuri makariri – intermediate annealing – trimming – foil rolling – tapahi – tākainga.
Engari mo te rereketanga o cu ihirangi, Ko etahi atu mahinga whakaputa o te tokotoru 8011 Ko nga konumohe konumohe ally he mea hanga i runga i nga waahanga tukanga rite. I whakamatauria te konumohe konumohe kua oti te whakamatau mo te mahi me te mahi tunu tunutunu. I tua atu, I tangohia nga tauira mo te whakamatautau anneing i 180 ℃, 200 ℃, 220 ℃, 240 ℃, 260 ℃ a 280 ℃ mo te 3h.

Ko te Pinhole me te Tohu Uara Uara o te konumohe konumohe ka whakamatauhia kia rite ki nga tikanga o GB3198-2010. Ko nga tauira e toru a nga tauira kua oti i tukuna i roto i te oumu paraoa mo te whakamatautau tunutunu. E ai ki te whakamahi i nga whakaritenga o nga kaihoko, Ko te pāmahana o te whakamātautau ātete tunutunu kua whakaritea ki 275 ℃, Na ko te waa tunutu te 75s.
Ko nga tauira o te taangata e mahia ana i runga i te paerewa GB3198-2010, Ko te roa o te rohe ko te 100mm, Na ko te toki roa o te tauira he rite tonu ki te ahunga hurihuri. I whakamatauria nga tauira whakaheke i runga i te miihini whakamatautau i te Universional CD II-1.

2 Nga hua whakamatautau me te tātari
Ko nga huringa e toru he hanganga riterite kaore he huanga o roto o roto penei i te wehenga. Ko te rahi o te kohanga o nga hori e toru kaore i te rereke, Na ko te rahi o te witi e tata ana 150 μm, e tutuki ana i nga whakaritenga o te tukanga hurihuri makariri me te tukanga a te konumohe konumohe.

Hei ako i te paanga o Cu ihirangi ki runga i nga paanga me te aukati tunutunu o te konumohe konumohe, E toru nga momo 8011 Ko nga hua o te konumohe konumohe me te rereke o Cu ihirangi i whakamatauria mo nga taonga miihini me nga mahi whakamatautau tunu i nga hua oti. Tokotoru 8011 Kakano katoa i raro i te hurihuri makariri, intermediate annealing, Na ka haere a Foil Rolling ki te tiki i nga momo konumohe kua oti o te matotoru rite. Ko te kaha o te alloy i whakaatu i te ahua nui o te pikinga o Cu ihirangi. I muri i te whakamatautau tunu, Tuhinga o mua 8011-3 He pai ki te teitei o Cu ihirangi e whakaitihia ana e 24.1%, Tuhinga o mua 8011-2 Kua heke te katoa 30.9%, Na te kaha kaha o te 8011-1 Kua heke te katoa 33.3% . Ka taea te kite i te pikinga o te ihirangi cu, Ko te pumau o te raau i muri i te kaha o te tunu ka piki haere.

I roto i te whakamatautau tunu, Mai i te mea ko te ātete o te tunutunu o te konumohe konumohe e tata ana ki te whanonga hou o te alloy, Hei whakataurite me te ako i te whanonga o te reti o te tokotoru 8011 Kakano, tokotoru 8011 Kua oti i a koe nga hua kua oti te whakarite 180 ℃, Anneling i 200 ℃ , 220 ℃ , 240 ℃ , 260 ℃ , 280 ℃ mo te 3h, Ko nga hua e whakaatu ana ko te pumau tonu o 8011-3 he teitei ake i tera o te koranu 8011-2 a 8011-1 koranu, 8011 I te ao taua me te waa. -3 alloys have less recrystallization and softening degree.

I tua atu, we also conducted dyne value test and pinhole test on three 8011 Kakano. The test results show that the dyne value and pinhole number of the three alloys all meet the standard.

Mo te 8011 koranu, within a certain range, with the increase of the trace alloying element Cu content, the solid solution strengthening effect is greater, so the strength of the 8011-3 alloy finished product is higher than that of the 8011-2 a 8011-1 Kakano.

Cu can form a small amount of CuA12 compound by solid solution precipitation in aluminum alloy. The CuA12 compound has an irregular and smooth shape, and is intermittently distributed in the grain boundary in a skeletal shape, which plays a role in dislocation pinning in the subsequent aluminum foil processing and deformation process; Ko te take ko te nuinga kei te nuinga o te waa o te otinga totoka i te al, he ngawari hoki ki te whakaemi i nga huringa. Ko te hanganga o te Corriolis Air Air e whakaiti ana i te wehewehe, ka whakaiti i te taunekeneke ngawari i waenga i nga ngota ngota me te whakakore, te tuku i nga reanga i roto i te ahua pumau, ka whakaiti i te maha o nga huringa neke, Ka aukati i te whakautu o nga whakakorekore, a ka aukati i te utu o te whakahekenga. Ka tipu te karaihe me te kūmara, Na reira e whakanui ake ana i te kaha o te orokohanga me te pāmahana whakahou i te konumohe kua oti.

Tuarua, Ko nga waahanga o nga huanga cules pea ka taea te whakariterite i nga waahanga tuarua, e arai nei i te heke o te nekehanga mo te hanga i roto i te mahanga ka whakatika me te aukati i te tipu o nga purapura o mua. I roto i te poto, within a certain range, Ko te whakapiki i te ihirangi o te waahanga taapiri ka taea e Cu te whakapiki i te pāmahana reihi o te alloy me te whakapai ake i te pumau wera o te alloy. Ka kitea ko te microAlloying tetahi o nga huarahi whakahirahira hei whakapai ake i te ātete wera o te hōu.

3 Whakamutunga
1) Ko te 8011-3 koranu me 8011-2 Ally i muri i te pikinga o te ihirangi CU ka tutuki i nga whakaritenga o nga kaihoko i nga ahuatanga o nga taonga miihini oti, Dyne Dyne, me te maha o nga pini.
2) Me te pikinga o te ihirangi cu, Tuhinga o mua 8011 Ka piki haere te ally; i te wa ano, Ko te pāmahana hurihuri o te hōulou ka piki haere.
3) I muri i te whakamatautau tunu i 240 ℃ / 75s, Tuhinga o mua 8011-3 He pai ki te teitei o Cu ihirangi e whakaitihia ana e 24.1%, Na te kaha kaha o te 8011-2 Kua heke te katoa 30.9%; Ko te kaha o te kaha kua heke iho 33.3%. 8011-3 Ka iti ake te rereketanga o te alloy i nga rawa atu i te 8011-2 a 8011-1. Ko te whakapiki i te ihirangi cu ka awhina ki te whakapai ake i te ātete tunu o te konumohe hinu oti.